1.No fire, No leakage.Vibration Test”電池不爆炸，不起火，不漏液?！闭駝樱?將滿電電芯放在振動實驗臺上，在 90~100mins 由 10 Hz 到 55 Hz 再到10Hz 以 1Hz/min 的速率變化，振幅為 0.8mm(0.060 英寸)進行振動實
驗。電芯在電芯的軸向和與電芯軸向垂直的兩個方向上振動。"      

2.The cell is to be dropped onto concrete ground from a height of 1.2 meter three times No explosion .電池從1.2米的高度下降到混凝土地面三次沒有爆炸。  

3.The pressure on the surface of the fully charged cell do not stop being raised until 17.2 Mpa when the cell is crushed by two flat surfaces.(Max13kN)"No explosion, No fire.”電池不爆炸，不起火?！盋rush Test擠壓滿充電電池被兩平板擠壓。擠壓的{zd0}壓強為17.2Mpa,{zd0}作用力為13kN。當達到{zd0}值即停止。

4.Heat Test高溫"The temperature of the baking box which contains cell is raised to 100±2℃ at a rate of 5℃/min and then holded for ten minutes."No explosion, No fire .”電池不爆炸，不起火。"滿充電電池在烘箱中測試。烘箱自室溫起以5℃/min的升溫速率升至100±2℃，并在100±2℃溫度下保持10min。         

5.Short-Circuit Test短路"After full charge, the positive and negative polarities are connected together by a copper wire whose resistance is less than or  equal to 0.1Ω.滿充電電池用電阻不大于0.1Ω的銅導線連接其正負極至電池體溫度接近室溫。"

6.Over-charge Test" "The cell is discharged following the standard discharge method. Apply a 5V power supply and a 3C charge current for 1.5hrs.”過充：電芯按照標準放電方式放完電后，采用 3C 電流 5V 電壓恒流恒壓充電。             
7.Standard environmental test condition/測試件        
   Unless otherwise specified, all tests stated in this Product Specification are conducted at below condition.                    
 Temperature：25±2℃   Relative humidity ：65±20%                       
 除特別說明外，本規(guī)格書中有測試均在以下環(huán)境中進行。                    
 溫度：25±2℃   相對濕度：65±20%                       