產品規(guī)格書 PRODUCT SPECIFICATION

    "The discharge capacity of contrast, under the conditions of different temperature in 25 ℃ under the condition of normal temperature after full charge of the battery, as shown in the table below normal temperature and high temperature to the capacity of 0.2 C to 6.0 V, low temperature is 0.2C to5.0 V  discharge capacity.the time between charging and discharging must beyond  3 hours.
    不同溫度件下的放電容量對比，即在25℃常溫件下電池滿充電后，在下表示常溫和高溫度下以0.2C放至6.0V的容量，低溫為0.2C放電至5.0V的容量。如果充電和放電溫度不是同溫度時，溫度變化的間隔時間要求是3小時。"                
 The pressure on the surface of the fully charged cell do not stop being raised until 17.2 Mpa when the cell is crushed by two flat surfaces.(Max13kN) ."No explosion, No fire.”
    擠壓：滿充電電池，被兩平板擠壓。擠壓的{zd0}壓強為17.2Mpa,{zd0}作用力為13kN。當達到{zd0}值即停止。電池不爆炸，不起火"   
 
The temperature of the baking box which contains cell is raised to 100±2℃ at a rate of 5℃/min and then holded for ten minutes. "No explosion, No fire .
高溫：滿充電電池在烘箱中測試。烘箱自室溫起以5℃/min的升溫速率升至100±2℃，并在100±2℃溫度下保持10min。電池不爆炸，不起火"   
   
After full charge, the positive and negative polarities are connected together by a copper wire whose resistance is less than or  equal to 0.1Ω. 
短路：滿充電電池用電阻不大于0.1Ω的銅導線連接其正負極至電池體溫度接近室溫。 
The cell is overcharged to 9.0V with a current of 1C and holded for 8 hours.
過充：電池在1C恒流恒壓下過充至9.0V，并保持8小時。       
Standard environmental test condition/測試件：                    
    Unless otherwise specified, all tests stated in this Product Specification are conducted at below condition.                    
 Temperature：25±2℃
   
    Relative humidity ：65±20%                       
 除特別說明外，本規(guī)格書中有測試均在以下環(huán)境中進行。                    
 溫度：25±2℃   相對濕度：65±20%            